Navegando por Autor "Lima, Ella Raquel do Vale Souza de"
Agora exibindo 1 - 3 de 3
- Resultados por página
- Opções de Ordenação
Tese Compósitos autolubrificantes de níquel sinterizados utilizando plasma DC(Universidade Federal do Rio Grande do Norte, 2024-02-28) Lima, Ella Raquel do Vale Souza de; Martinelli, Antônio Eduardo; https://orcid.org/0000-0003-3885-9104; http://lattes.cnpq.br/0022988322449627; https://orcid.org/0009-0005-6003-4338; http://lattes.cnpq.br/6548985093027325; Neves, Guilherme Oliveira; Binder, Cristiano; Nascimento, Rubens Maribondo do; Gomes, Uilame UmbelinoO presente trabalho teve o intuito de avaliar os respectivos efeitos de diferentes lubrificantes sólido dispersos em todo o volume na matriz de níquel, produzidos via metalurgia do pó. Foram utilizados como lubrificante sólido o grafite, o qual foi introduzido na matriz pela rota convencional na etapa de mistura simples, e o lubrificante gerado “in situ” pela dissociação de carbeto de silício (SiC) durante a sinterização. Nas misturas o teor de grafite e SiC foi fixado em 10% em volume, a conformação das amostras foi realizada por compactação uniaxial a uma pressão de 600MPa, a sinterização ocorreu em reator a plasma DC e forno convencional, diferentes temperaturas de sinterização foram aplicadas (800 ºC, 900 ºC e 1000 ºC). O estudo da microestrutura e dureza destes materiais foram realizados utilizando as análises de densidades a verde e do sinterizado, DRX, Espectroscopia Raman, MO, MEV/FEG-EDS e microdureza Vickers, as quais mostraram a influência dos diferentes lubrificantes sólidos, da temperatura e equipamentos de sinterização na formação dos compósitos, na continuidade da matriz de níquel e na cinética de dissociação do SiC. O silício resultante da dissociação do carbeto de silício enriquece a matriz de níquel, na qual a solubilidade do carbono varia com a temperatura, contudo o carbono retido precipita e permanece na forma de grafite. A adição de lubrificante sólido na matriz promoveu redução na densidade do sinterizado. O aumento da temperatura de sinterização aumentou a densificação e reduziu a porosidade. A sinterização a 1000 ºC promoveu maiores valores de microdureza. Os depósitos de grafite aumentaram nas amostras contendo SiC com a elevação da temperatura. Com base nestas informações, foram analisadas o comportamento tribológico dos materiais sinterizados a 1000 ºC. Os compósitos contendo lubrificante sólido obtidos pela rota convencional apresentaram os menores valores de coeficiente de atrito e taxa de desgaste. Os aspectos microestruturais e de dureza indicam uma semelhança entre os processos de sinterização a plasma em regime anormal (DC) e em forno tubular.Artigo Effect of desulfurization of diesel and its blends with biodiesel on metallic contact(ABM, ABC, ABPol, 2014-07-22) Alves, Salete Martins; Mello, Valdicleide SIlva e; Lima, Ella Raquel do Vale Souza de; Oliveira, Marcos Vinycius de AraújoThe current environmental scenario has required changes in fuel nature, in order to minimize the harmful effects caused by sulfur in diesel. However, reductions in sulfur content promote loss of its lubricity and consequently wear in the injection system of the diesel engine. This study aimed to investigate the influence of sulfur minimization on fuel lubricity and wear of metallic disks. The fuel tribological analysis was carried out in HFRR equipment in accordance with ASTM D 6079-04. The tested fuels were diesel oil with 50, 500 and 1800 ppm sulfur, and their blends of soybean and sunflower biodiesel (5, 20 and 100% in volume). The results showed an increase of disks wear with reduction of sulfur content when lubricated with pure diesel. This fact was decreased when biodiesel was added to all concentrationsDissertação Sinterização de compósitos de Ni/SiC a partir de NiO(2018-09-04) Lima, Ella Raquel do Vale Souza de; Martinelli, Antonio Eduardo; ; ; Fernandes, Maria Roseane de Pontes; ; Peres, Maurício Mhirdaui;Compósitos de matriz metálica de níquel reforçados por partículas de carbeto são considerados materiais de engenharia promissores por apresentarem propriedades como resistência mecânica associada à resistência à corrosão e resistência ao desgaste em altas temperaturas. Porém, a toxicidade do níquel é um aspecto limitante no uso desse pó. Uma alternativa à produção de compósitos sinterizados com matriz de níquel é por meio do emprego do NiO. Neste trabalho foi estudado a produção de compósitos Ni-SiC partindo da matriz de NiO pelo processo de redução do óxido durante a etapa de sinterização. Foram investigados os efeitos da carga de compactação no comportamento dilatométrico de misturas Ni-SiC. Os pós de NiO com tamanho médio de partículas de 14 µm foram misturados a 0%, 3%, 5%, 10% e 20% em massa de SiC com tamanho médio de partículas de 14,75 µm. A mistura foi realizada em moinho de alta energia tipo atrittor durante 1h. As misturas foram granuladas em tambor, com 1,5% em massa de parafina diluída em hexano. A compactação uniaxial foi realizada utilizando pressão de 200 MPa e 400 MPa. As peças foram sinterizadas em dilatômetro com taxa de aquecimento de 5ºC e 10ºC/min. Foram avaliados os perfis dilatométricos e determinadas as densidades das amostras. Foi avaliada a influência da taxa de aquecimento na sinterização e da pressão de compactação na densificação e microestrutura. A partir dos resultados obtidos foi possível concluir que: as imagens obtidas por MEV-FEG das misturas de NiO-SiC comprovaram distribuição homogênea dos carbetos na matriz de óxido de níquel. As amostras compactadas com pressão 400MPa apresentaram maior densidade; as curvas de dilatometria mostraram que o SiC favoreceu a sinterização do Ni, e as amostras sinterizadas com taxa de aquecimento menor apresentaram maior retração. A adição de 10% de SiC na matriz de Ni permitiu o endurecimento com maior homogeneidade microestrutural e melhor continuidade da matriz, apresentou maior valor de dureza e boa densidade superficial comprovada pelas imagens obtidas por MEV.